Details of heat resistant EP conveyor belt :
Models:
Mode1: able to with stand the test temperature of less than 100°C, code S1
Mode2: able to with stand the test temperature of less than 125°C, code S2
Mode3: able to with stand the test temperature of less than 150°C, code S3
Mode4: able to with stand the test temperature of less than 175°C, code S4
Heat resistant conveyor belt is mainly used to transport high temperature materials, such as sintering ore, hot coke, clinker, hot casting and so on. According to the manifestation of the heat resistant belt breakage until to lose transportation ability and the heat resistant grading, we use EDPM or SBR as the covering layer rubber, and high modulus low shrinkage polyester or cotton canvas as the strong layer. It can use the heat resistant woven glass fabric between the cover rubber and the layers, so as to improve the working life of the heat resistant conveyor belt. We can make it into endless conveyor belt as per cllients' requirement.
|
The physical and mechanical properties of the heat resistant covering layer after tested should be in accordance with the following table: |
|||||
| Project | The type | ||||
| T1 | T2 | T3 | T4 | ||
| Change the range | |||||
| Hardness | Draw the intensity | 20 | 20 | 20 | 20 |
| Maximum after wearing out | 85 | ||||
| Draw the intensity |
The minimum value Mpa after wearing out |
12 | 10 | 5 | 5 |
| Performance rate of change /% | -25 | -30 | -40 | -40 | |
| Break person who extend | Performance rate of change /% | -50 | -50 | -55 | -55 |
| After aging rate of change /% | 200 | 200 | 180 | 180 | |
The heat resistance conveyor belt physical property of the cover rubber after heat test shall conform to the values specified in the table.
| Item | type | ||||||
| type I | type II | type III | |||||
| variable range | |||||||
| Hardness | Difference before and after ageing (IRHD) | ±20 | |||||
| Max. Value after ageing (IRHD) | 85 | ||||||
| Tensile strength | variable rate in performance <= | 25 | 30 | 40 | |||
| Min. value after ageing Mpa | 12 | 10 | 5 | ||||
| Rate of elongation at break | variable rate in performance% <= | 50 | 55 | ||||
| Min. value after ageing | 200 | 180 | |||||
The heat resistance conveyor belt abrasive wear of the cover rubber
| Type Item level | Abrasive wear | ||
| type I | type II | type III | |
| First quality | 0.8 | 1 | 1 |
| accepts | 1 | 1.2 | 1.2 |
The heat resistance conveyor belt layer to layer adhesion strength
| Item |
interlayer of cloth |
cover layer and cloth interlayer | |
|
Thickness of the cover layer ≤1.5mm |
Thickness of the cover layer >1.5mm |
||
|
The average value of the longitudinal specimen shall be no less than |
3 | 2.2 | 2.6 |
|
The peak value of the longitudinal specimen |
2 | 1.6 | 2.0 |
Pictures of heat resistant EP conveyor belt : 
Inspetion Equipment
workshop
For more details,please inquiry us!
Polyester conveyor belt, (EP)
Nylon conveyor belt, (NN)
Cotton conveyor belt, (CC)
Chevron conveyor belt, (C5 C10 and C15)
Oil Resistance conveyor belt, (OR and MOR)
Hot Resistance conveyor belt, (HR)
Fire Resistance conveyor belt, (FR/PVC/PVG)
Heat Resistance conveyor belt, (OHR/ OFR)
Cold Resistance conveyor belts, (CR)
Endless belts
Conveyor roller, idler
Conveyor Pulley, frame,bracket etc
){kind=link}